- Two-part, black electrically conductive RTV silicone
- 10:1 Mix Ratio (Part A:B)
Applications
- For applications requiring low outgassing and minimal volatile condensables under extreme operating conditions to avoid condensation in sensitive devices
- Use for RFI and EMI shielding in electronic and space applications
- Use to adhere covers onto housings or for any application where grooves and other configurations require a flowable to limited flow material
- For applications requiring a broader operating temperature range
Meets or exceeds the ASTM E 595 low outgas specifications outlined
in NASA SP-R-0022A and European Space Agency PSS-014-702, with
a TML of ≤1% and CVCM of ≤0.1%
| Property |
Average result |
| Volume Resistivity |
2.5 ohmcm
|
| Cure System |
Platinum |
| Durometer |
75 Type A
|
| Tensile |
475 psi
|
| Appearance |
Black |
| Cte |
580 ppm/C
|
| Cure |
30 minutes / 150 C |
| Elongation |
90 %
|
| Lap Shear |
250 psi
|
| Mix Ratio |
10:1 |
| Specific Gravity |
1.19 |
| Work Time |
2 hours
|
| Comment |
2.5 ohmcm, *4) Primed Lap Shear 250 psi (1.7 MPa), Carbon Fiber Filled |
| Property |
Average result |
| Volume Resistivity |
2.5 ohmcm
|
| Cure System |
Platinum |
| Durometer |
75 Type A
|
| Tensile |
3.28 MPa
|
| Appearance |
Black |
| Cte |
580 ppm/C
|
| Cure |
30 minutes / 150 C |
| Elongation |
90 %
|
| Lap Shear |
1.72 MPa
|
| Mix Ratio |
10:1 |
| Specific Gravity |
1.19 |
| Work Time |
2 hours
|
| Comment |
2.5 ohmcm, *4) Primed Lap Shear 250 psi (1.7 MPa), Carbon Fiber Filled |
Display in metric units
The above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.