R-2182

LOW COEFFICIENT OF FRICTION SILICONE COATING

 

Description

  • Two-part silicone elastomer dispersed in xylene
  • Cures to a smooth silicone film that decreases the coefficient of friction (CoF) compared to the uncoated silicone and increases abrasion resistance for moving, sliding, and rubbing parts
  • Provides adhesion to silicone substrates that results in a reduction of surface tack
  • 1:1 Mix Ratio (Part A: Part B)

Applications

  • To provide a heat-cured, low-friction coating on cured silicone substrates
  • Apply by spraying for best results (dipping may also be utilized)

Product Details

Property Average result
Appearance A: Transluscent / B: Translucent to Opaque
Non-Volatile Content 25 %
Viscosity 24 cP
Cure 5 minutes / RTV
Cure System Platinum
Mix Ratio 1:1
Post Cure 5 minutes / 150 C
Specific Gravity 0.96
Work Time >24 hours
Comment Requires minimum heat to cure. Acetic acid cure by-product therefore not recommended where corrosion is of concern.
Display in metric units
 

The above properties are tested on a lot-to-lot basis. Do not use as a basis for preparing specifications. Please contact NuSil Technology for assistance and recommendations in establishing particular specifications.

Optoelectronics
Specialty Silicones for Displays

The NuSil™ line of optoelectronic silicones enable device manufacturers from smart phones to stadium screens and everything in between to create next-generation displays that are sharper, brighter and more rugged.

Read More